Table 1 main performances and indicators of high strength polyester dipped line (be used as brake tubes,general oil transfer pipe) |
ITEM |
UNIT |
1000D |
1260D |
1500D |
2000D |
3000D |
4000D |
Breaking strength |
N |
>75 |
>95 |
>110 |
>150 |
>220 |
>290 |
Elongation at breaking |
% |
9.0±1.0 |
9.0±1.0 |
9.0±1.0 |
9.0±1.0 |
9.0±1.0 |
9.0±1.0 |
Diameter |
mm |
0.21±0.1 |
0.25±0.1 |
0.28±0.1 |
0.31±0.1 |
0.45±0.1 |
0.60±0.1 |
Twist Degree |
T/m |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
U.weight |
G/100m |
12±1 |
15±1 |
18±1 |
24±2 |
36±2 |
48±2 |
Shrinkage at dry, heat condition & with loads |
% |
3.0±0.7 |
3.0±0.7 |
3.0±0.7 |
3.0±0.7 |
3.0±0.7 |
3.0±0.7 |
Adhesive force |
N/cm |
＞60 |
>63 |
>75 |
＞80 |
＞120 |
＞150 |
Note: cohesive force test base rubber is chlorine, styrene-butadiene and chloroprene rubber, etc.
|
Table 2 main performances and indicators of high strength polyester dipped line(be used as automobile air conditioning tube) |
ITEM |
UNIT |
1000D |
1260D |
1500D |
2000D |
3000D |
4000D |
Breaking strength |
N |
>75 |
>95 |
>110 |
>150 |
>220 |
>290 |
Elongation at breaking |
% |
18±2 |
18±2 |
18±2 |
18±2 |
18±2 |
18±2 |
Diameter |
mm |
0.21±0.1 |
0.25±0.1 |
0.28±0.1 |
0.31±0.1 |
0.45±0.1 |
0.60±0.1 |
Twist Degree |
T/m |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
U.weight |
g/100m |
12±1 |
15±1 |
18±1 |
24±2 |
36±2 |
48±2 |
Shrinkage at dry, heat condition & with loads |
% |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
Adhesive force |
N/cm |
＞50 |
>63 |
>75 |
＞80 |
＞120 |
＞150 |
Note:EPDM rubber adhesion strength
 |
 |
Table 3 main performances and indicators of high strength polyester dipped line(be used as automobile pipes) |
ITEM |
UNIT |
1000D |
1260D |
1500D |
2000D |
3000D |
4000D |
Breaking strength |
N |
>75 |
>95 |
>110 |
>150 |
>220 |
>290 |
Elongation at breaking |
% |
18±2 |
18±2 |
18±2 |
18±2 |
18±2 |
18±2 |
Diameter |
mm |
0.21±0.1 |
0.25±0.1 |
0.28±0.1 |
0.31±0.1 |
0.45±0.1 |
0.60±0.1 |
Twist Degree |
T/m |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
U.weight |
g/100m |
12±1 |
15±1 |
18±1 |
24±2 |
36±2 |
48±2 |
Shrinkage at dry, heat condition & with loads |
% |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
 |
Table 4 main performances and indicators of high strength polyester dipped line(be used as automobile pipes,after dipping to increase the adhesion strength, at the same time meet the knitting process) |
ITEM |
UNIT |
1000D |
1260D |
1500D |
2000D |
3000D |
4000D |
Breaking strength |
N |
>75 |
>95 |
>110 |
>150 |
>220 |
>290 |
Elongation at breaking |
% |
18±2 |
18±2 |
18±2 |
18±2 |
18±2 |
18±2 |
Diameter |
mm |
0.21±0.1 |
0.25±0.1 |
0.28±0.1 |
0.31±0.1 |
0.45±0.1 |
0.60±0.1 |
Twist Degree |
T/m |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
U.weight |
g/100m |
12±1 |
15±1 |
18±1 |
24±2 |
36±2 |
48±2 |
Shrinkage at dry, heat condition & with loads |
% |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
Adhesive force |
N/cm |
＞40 |
>55 |
>65 |
＞70 |
＞100 |
＞120 |
 |
Table 5 main performances and indicators of high strength polyester dipped line |
ITEM |
UNIT |
1000D |
1260D |
1500D |
2000D |
3000D |
4000D |
Breaking strength |
N |
>60 |
>76 |
>90 |
>120 |
>180 |
>240 |
Elongation at breaking |
% |
18±2 |
18±2 |
18±2 |
18±2 |
18±2 |
18±2 |
Diameter |
mm |
0.21±0.1 |
0.25±0.1 |
0.28±0.1 |
0.31±0.1 |
0.45±0.1 |
0.60±0.1 |
Twist Degree |
T/m |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
U.weight |
g/100m |
12±1 |
15±1 |
18±1 |
24±2 |
36±2 |
48±2 |
Shrinkage at dry, heat condition & with loads |
% |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
Adhesive force |
N/cm |
＞50 |
>63 |
>75 |
＞80 |
＞120 |
＞150 |
 |
Table 4 main performances and indicators of high strength polyester dipped line(be used as automobile pipes,
feather-like surface, increasing adhesion strength and resolve of the production process in chaos ) |
ITEM |
UNIT |
1000D |
1260D |
1500D |
2000D |
3000D |
4000D |
Breaking strength |
N |
>60 |
>76 |
>90 |
>120 |
>180 |
>240 |
Elongation at breaking |
% |
18±2 |
18±2 |
18±2 |
18±2 |
18±2 |
18±2 |
Diameter |
mm |
0.21±0.1 |
0.25±0.1 |
0.28±0.1 |
0.31±0.1 |
0.45±0.1 |
0.60±0.1 |
Twist Degree |
T/m |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
100±10 |
U.weight |
g/100m |
12±1 |
15±1 |
18±1 |
24±2 |
36±2 |
48±2 |
Shrinkage at dry, heat condition & with loads |
% |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
＜1.2 |
 |
 |
Color Line |
Performance indicators customized according to customer requirements. |
|